BOLT |
Grade |
C(%) |
Mn(%) |
P(%) |
S(%) |
Si(%) |
ASTM A193 Gr. B7 |
0.37~0.49 |
0.65~1.10 |
0.035 Max. |
0.040 Max. |
0.15~0.35 |
ASTM A193 Gr. B7M |
0.37~0.49 |
0.65~1.10 |
0.035 Max. |
0.040 Max. |
0.15~0.35 |
ASTM A193 Gr. B16 |
0.39~0.47 |
0.45~0.70 |
0.035 Max. |
0.040 Max. |
0.15~0.35 |
ASTM A193 Gr. B8 |
0.08 Max. |
2.00 Max. |
0.045 Max. |
0.030 Max. |
1.00 Max. |
ASTM A193 Gr. B8M |
0.08 Max. |
2.00 Max. |
0.045 Max. |
0.040 Max. |
1.00 Max. |
ASTM A320 Gr. L7 |
0.38~0.48 |
0.75~1.00 |
0.035 Max. |
0.030 Max. |
0.15~0.35 |
ASTM A320 Gr. B8 |
0.08 Max. |
2.00 Max. |
0.045 Max. |
0.030 Max. |
1.00 Max. |
ASTM A320 Gr. B8M |
0.08 Max. |
2.00 Max. |
0.045 Max. |
0.030 Max. |
1.00 Max. |
JIS G4105 SCM 440 |
0.38~0.43 |
0.30~0.85 |
0.030 Max. |
0.030 Max. |
0.15~0.35 |
JIS G4107 SNB 5 |
0.10 Min. |
1.00 Min. |
0.040 Max. |
0.030 Max. |
1.00 Max. |
JIS G4107 SNB 7 |
0.38~0.48 |
0.75~1.00 |
0.040 Max. |
0.040 Max. |
0.20~0.35 |
JIS G4107 SNB 16 |
0.36~0.44 |
0.45~0.70 |
0.040 Max. |
0.040 Max. |
0.20~0.35 |
NUT |
ASTM A194 Gr. 2H |
0.40 Min. |
1.00 Max. |
0.040 Max. |
0.050 Max. |
0.40 Max. |
ASTM A194 Gr. 2HM |
0.40 Min. |
1.00 Max. |
0.040 Max. |
0.050 Max. |
0.40 Max. |
ASTM A194 Gr. 4 |
0.40~0.50 |
0.70~0.90 |
0.035 Max. |
0.040 Max. |
0.15~0.35 |
ASTM A194 Gr. 7 |
0.39~0.49 |
0.65~1.10 |
0.040 Max. |
0.040 Max. |
0.15~0.35 |
ASTM A194 Gr. 8 |
0.08 Max. |
2.00 Max. |
0.045 Max. |
0.030 Max. |
1.00 Max. |
ASTM A194 Gr. 8M |
0.08 Max. |
2.00 Max. |
0.045 Max. |
0.030 Max. |
1.00 Max. |
JIS G4051 S45C |
0.42~0.48 |
0.60~0.90 |
0.030 Max. |
0.035 Max. |
0.15~0.35 | |
BOLT |
Grade |
Cr(%) |
Mo(%) |
V(%) |
Ni(%) |
Min. Tempering Temperature ℉(℃) |
ASTM A193 Gr. B7 |
0.75~1.20 |
0.15~0.25 |
|
|
1,100(593℃) |
ASTM A193 Gr. B7M |
0.75~1.20 |
0.15~0.25 |
|
|
1,150(620℃) |
ASTM A193 Gr. B16 |
0.80~1.15 |
0.50~0.65 |
0.25~0.35 |
|
1,200(650℃) |
ASTM A193 Gr. B8 |
18.00~20.00 |
|
|
8.00~10.50 |
Carbide Solution Treated |
ASTM A193 Gr. B8M |
16.00~18.00 |
2.00~3.00 |
|
10.00~14.00 |
Carbide Solution Treated |
ASTM A320 Gr. L7 |
0.80~1.10 |
0.15~0.25 |
|
|
|
ASTM A320 Gr. B8 |
18.00~20.00 |
|
|
8.00~10.50 |
|
ASTM A320 Gr. B8M |
16.00~18.00 |
2.00~3.00 |
|
|
|
JIS G4105 SCM 440 |
0.90~1.20 |
0.15~0.30 |
|
|
530 ~ 630℃ |
JIS G4107 SNB 5 |
4.00~6.00 |
0.40~0.65 |
|
|
(595℃) |
JIS G4107 SNB 7 |
0.80~1.10 |
0.15~0.25 |
|
|
(595℃) |
JIS G4107 SNB 16 |
0.80~1.15 |
0.50~0.65 |
0.25~0.35 |
|
(650℃) |
NUT |
ASTM A194 Gr. 2H |
|
|
|
|
850(455℃) |
ASTM A194 Gr. 2HM |
|
|
|
|
1,150(620℃) |
ASTM A194 Gr. 4 |
|
0.20~0.30 |
|
|
1,100(595℃) |
ASTM A194 Gr. 7 |
0.75~1.20 |
0.15~0.25 |
|
|
1,100(595℃) |
ASTM A194 Gr. 8 |
18.00~20.00 |
|
|
8.00~10.50 |
|
ASTM A194 Gr. 8M |
16.00~18.00 |
2.00~3.00 |
|
10.00~14.00 |
|
JIS G4051 S45C |
|
|
|
|
550~650℃ | | |